Evaluación de las propiedades mecánicas de una mezcla densa en caliente modificada con asfaltita

Abstract

The strength under monotonic load, resilient modulus and rutting were evaluated on a hot-mix asphalt (HMA) modified with a natural asphaltite. Additionally, the influence of the environmental conditions of Bogotá D.C., was evaluated during two years on the mechanical properties of a modified asphalt mixture. The results show that the mechanical properties evaluated were better for the HMA mixes modified in compared with those with neat asphalts. The asphaltite produces higher mechanical resistance in HMA. The general tendency of the mixtures is increase the modulus with time due to aging of the asphalt cement. However, modified mixtures with AC 60-70, decrease in stiffness during the first months

El trabajo evaluó en laboratorio la resistencia mecánica bajo carga monotónica, el módulo resiliente y la resistencia a la deformación permanente que experimenta una mezcla asfáltica cuando se modifica con una asfaltita. Adicionalmente, fue evaluada durante dos años, la influencia del medio ambiente de la ciudad de Bogotá D.C., sobre las propiedades mecánicas de la mezcla modificada. Se concluye que la resistencia mecánica de la mezcla asfáltica modificada incrementa en comparación con la convencional. La tendencia general de las mezclas con el tiempo de exposición al medio ambiente de Bogotá D.C., es experimentar un aumento en los valores de rigidez debido principalmente a procesos de endurecimiento por envejecimiento del ligante asfáltico. Sin embargo, para el caso de las mezclas modificadas y fabricadas con CA 6070 en los primeros cinco meses de exposición, la rigidez disminuye.